ASTM D1329 Standard Test Method for Evaluating Rubber Property-Retraction at Lower Temperatures (TR Test)
Данный раздел/документ содержится в продуктах:
- Техэксперт: Машиностроительный комплекс
- Картотека зарубежных и международных стандартов
- ASTM MNL11 Manual on Drilling, Sampling, and Analysis of Coal
- ASTM D121 REV A Standard Terminology of Coal and Coke
- 01
- ASTM D121 REV A Standard Terminology of Coal and Coke
- 01.040
- ASTM D121 REV A Standard Terminology of Coal and Coke
- 01.040.73
- ASTM D1412 Standard Test Method for Equilibrium Moisture of Coal at 96 to 97 Percent Relative Humidity and 30°C
- ASTM D5192 Standard Practice for Collection of Coal Samples from Core
- ASTM D4596 Standard Practice for Collection of Channel Samples of Coal in a Mine
- ASTM D2234/D2234M Standard Practice for Collection of a Gross Sample of Coal
- SAE J1085 Testing Dynamic Properties of Elastomeric Isolators
- Картотека зарубежных и международных стандартов
ASTM International
Standard Test Method for Evaluating Rubber Property-Retraction at Lower Temperatures (TR Test)
N D1329
Annotation
This test method describes a temperature-retraction procedure for rapid evaluation of crystallization effects and for comparing viscoelastic properties of rubber and rubber-like materials at low temperatures. This test method is useful when employed in conjunction with other low-temperature tests for selection of materials suitable for low-temperature service.
The values stated in SI units are to be regarded as the standard. The values given in parentheses are for information only.
This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.
Автоматический перевод:
Стандартный метод испытаний для оценки резинового имущественного сокращения при более низких температурах (испытание TR)
Этот метод тестирования описывает процедуру температурного сокращения для быстрой оценки эффектов кристаллизации и для сравнения вязкоупругих свойств резиновых и подобных резине материалов при низких температурах. Этот метод тестирования полезен, когда используется в сочетании с другими тестами низкой температуры для выбора материалов, подходящих для сервиса низкой температуры.