ASTM C115/C115M Standard Test Method for Fineness of Portland Cement by the Turbidimeter
Данный раздел/документ содержится в продуктах:
- Техэксперт: Машиностроительный комплекс
- Картотека зарубежных и международных стандартов
- ASTM D6935 Standard Test Method for Determining Cement Mixing of Emulsified Asphalt
- ASTM C816 Standard Test Method for Sulfur in Graphite by Combustion-Iodometric Titration Method
- ASTM F2191/F2191M Standard Specification for Packing Material, Graphitic or Carbon Braided Yarn
- ASTM C135 Standard Test Method for True Specific Gravity of Refractory Materials by Water Immersion
- ASTM C1240 Standard Specification for Silica Fume Used in Cementitious Mixtures
- ASTM C135 Standard Test Method for True Specific Gravity of Refractory Materials by Water Immersion
- ASTM F2191/F2191M Standard Specification for Packing Material, Graphitic or Carbon Braided Yarn
- 71
- ASTM C816 Standard Test Method for Sulfur in Graphite by Combustion-Iodometric Titration Method
- ASTM F2191/F2191M Standard Specification for Packing Material, Graphitic or Carbon Braided Yarn
- ASTM C135 Standard Test Method for True Specific Gravity of Refractory Materials by Water Immersion
- ASTM C1240 Standard Specification for Silica Fume Used in Cementitious Mixtures
- ASTM C135 Standard Test Method for True Specific Gravity of Refractory Materials by Water Immersion
- ASTM F2191/F2191M Standard Specification for Packing Material, Graphitic or Carbon Braided Yarn
- 71.060
- ASTM C816 Standard Test Method for Sulfur in Graphite by Combustion-Iodometric Titration Method
- ASTM F2191/F2191M Standard Specification for Packing Material, Graphitic or Carbon Braided Yarn
- ASTM C135 Standard Test Method for True Specific Gravity of Refractory Materials by Water Immersion
- ASTM C1240 Standard Specification for Silica Fume Used in Cementitious Mixtures
- ASTM C135 Standard Test Method for True Specific Gravity of Refractory Materials by Water Immersion
- ASTM F2191/F2191M Standard Specification for Packing Material, Graphitic or Carbon Braided Yarn
- ASTM C816 Standard Test Method for Sulfur in Graphite by Combustion-Iodometric Titration Method
- ASTM C816 Standard Test Method for Sulfur in Graphite by Combustion-Iodometric Titration Method
- ASTM F2191/F2191M Standard Specification for Packing Material, Graphitic or Carbon Braided Yarn
- ASTM C135 Standard Test Method for True Specific Gravity of Refractory Materials by Water Immersion
- ASTM C1240 Standard Specification for Silica Fume Used in Cementitious Mixtures
- ASTM C135 Standard Test Method for True Specific Gravity of Refractory Materials by Water Immersion
- ASTM C135 Standard Test Method for True Specific Gravity of Refractory Materials by Water Immersion
- ASTM C1240 Standard Specification for Silica Fume Used in Cementitious Mixtures
- ASTM C1240 Standard Specification for Silica Fume Used in Cementitious Mixtures
- ASTM C1005 Standard Specification for Reference Masses and Devices for Determining Mass and Volume for Use in the Physical Testing of Hydraulic Cements
- ASTM C596 Standard Test Method for Drying Shrinkage of Mortar Containing Hydraulic Cement
- ASTM C226 Standard Specification for Air-Entraining Additions for Use in the Manufacture of Air-Entraining Hydraulic Cement
- ASTM C465 Standard Specification for Processing Additions for Use in the Manufacture of Hydraulic Cements
- Картотека зарубежных и международных стандартов
ASTM International
Standard Test Method for Fineness of Portland Cement by the Turbidimeter
N C115/C115M
Annotation
This test method covers determination of the fineness of portland cement as represented by a calculated measure of specific surface, expressed as square centimetres of total surface area per gram, or square metres of total surface area per kilogram, of cement, using the Wagner turbidimeter.2
This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.
The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard. Values in SI units [or inch-pound units] shall be obtained by measurement in SI units [or inch-pound units] or by appropriate conversion, using the Rules for Conversion and Rounding given in IEEE/ASTM SI 10 of measurements made in other units. Values are stated in SI units when inch-pound units are not used in practice.
2 The sole source of supply of the apparatus known to the committee at this time is the Wagner turbidimeter. If you are aware of alternative suppliers, please provide this information to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of the responsible technical committee,1 which you may attend. This turbidimeter was developed by L. A. Wagner, Research Associate of the Cement Reference Laboratory, National Institute of Standards and Technology, Washington, DC. A description of the apparatus and the original mathematical derivations of formulas used are given in the paper:Wagner, L. A., "A Rapid Method for the Determination of the Specific Surface of Portland Cement," Proceedings , ASTM, ASTEA, Vol 33, Part II, 1933, p. 553.