Plastics - Determination of dynamic mechanical properties - Part 11: Glass transition temperature - First Edition
 N 6721-11

Annotation

This part of ISO 6721 specifies methods for determining a value of the glass transition temperature (Tg) from the dynamic mechanical properties measured during a linear temperature scan under heating conditions. The glass transition temperature is an indicator of the transition from a glassy state to a rubbery state.

Usually referred to as dynamic mechanical analysis (DMA), the methods and their associated procedures can be applied to unreinforced and filled polymers, foams, rubbers, adhesives and fibre-reinforced plastics/composites. Different modes (e.g. flexure, compression, tension) of dynamic mechanical analysis can be applied, as appropriate, to the form of the source material.

NOTE For tests undertaken in the flexure or torsion mode, an additional procedure is included to identify the severity of the influences of thermal lag on the measured data (see Annex B).

Автоматический перевод:

Пластмассы - Определение динамических механических свойств - Часть 11: Температура стеклования - Первый Выпуск

Эта часть ISO 6721 определяет методы для определения значения температуры стеклования (Tg) от динамических механических свойств, измеренных во время линейного температурного просмотра при нагревающихся условиях. Температура стеклования является индикатором перехода от застеклованного состояния до высокоэластического состояния.