SNV SN EN ISO 4628-8 Paints and varnishes - Evaluation of degradation of coatings - Designation of quantity and size of defects, and of intensity of uniform changes in appearance - Part 8: Assessment of degree of delamination and corrosion around a scribe or other artificial defect
Данный раздел/документ содержится в продуктах:
- Техэксперт: Машиностроительный комплекс
- Картотека зарубежных и международных стандартов
- BSI BS EN 2434-003 Aerospace series - Paints and varnishes - Two component cold curing polyurethane finish Part 003: Flexible and high fluid resistance for interior
- 49
- BSI BS EN 2434-003 Aerospace series - Paints and varnishes - Two component cold curing polyurethane finish Part 003: Flexible and high fluid resistance for interior
- 49.040
- BSI BS EN 2434-003 Aerospace series - Paints and varnishes - Two component cold curing polyurethane finish Part 003: Flexible and high fluid resistance for interior
- BSI BS EN 2436-003 Paints and varnishes Corrosion resistant chromate-free two component cold curing primer Part 003: High corrosion and fluid resistance
- BSI BS EN 2436-003 Paints and varnishes Corrosion resistant chromate-free two component cold curing primer Part 003: High corrosion and fluid resistance
- BSI BS EN 2436-003 Paints and varnishes Corrosion resistant chromate-free two component cold curing primer Part 003: High corrosion and fluid resistance
- ISO 3270 Paints and Varnishes and Their Raw Materials - Temperatures and Humidities for Conditioning and Testing Third Edition
- Картотека зарубежных и международных стандартов
Schweizerische Normen-Vereinigung
Paints and varnishes - Evaluation of degradation of coatings - Designation of quantity and size of defects, and of intensity of uniform changes in appearance - Part 8: Assessment of degree of delamination and corrosion around a scribe or other artificial defect
N SN EN ISO 4628-8
Annotation
This part of ISO 4628 specifies a method for assessing delamination and corrosion around a scribe or other artificial defect on a coated panel or other coated test specimen, caused by a corrosive environment.
This part of ISO 4628 does not cover evaluation of pitting corrosion or pit depth.
NOTE 1 Examples of corrosive environments are artificial atmospheres such as salt spray, as used in the test method specified in ISO 9227,[7] and sea water immersion as used in the test method specified in ISO 15711.[8] Natural environments can also be used.
NOTE 2 The extent of other defects can also be determined at the same time as delamination and corrosion. Methods are given as follows:
— blistering in accordance with ISO 4628-2;[2]
— rusting in accordance with ISO 4628-3;[3]
— cracking in accordance with ISO 4628-4;[4]
— flaking in accordance with ISO 4628-5;[5]
— filiform corrosion in accordance with ISO 4628-10.[6]
Автоматический перевод: