Standard Practice for Measuring Viscosity of Glass Above the Softening Point
 N C965

Annotation

This practice covers the determination of the viscosity of glass above the softening point through the use of a platinum alloy spindle immersed in a crucible of molten glass. Spindle torque, developed by differential angular velocity between crucible and spindle, is measured and used to calculate viscosity. Generally, data are taken as a function of temperature to describe the viscosity curve for the glass, usually in the range from 1 to 106 Pa·s.

Two procedures with comparable precision and accuracy are described and differ in the manner for developing spindle torque. Procedure A employs a stationary crucible and a rotated spindle. Procedure B uses a rotating crucible in combination with a fixed spindle.

This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

Автоматический перевод:

Общепринятая практика для измерения вязкости стекла выше точки размягчения

Эта практика покрывает определение вязкости стекла выше точки размягчения с помощью платинового шпинделя сплава, погруженного в суровое испытание расплавленного стекла. Шпиндельный вращающий момент, развитый отличительной угловой скоростью между суровым испытанием и шпинделем, измеряется и используется для вычисления вязкости. Обычно данные взяты в качестве функции температуры для описания кривой вязкости для стакана, обычно в диапазоне от 1 до 106 Па · s.