ASTM D7255 Standard Test Method for Abrasion Resistance of Leather (Rotary Platform, Abraser Method)
Данный раздел/документ содержится в продуктах:
- Техэксперт: Машиностроительный комплекс
- Картотека зарубежных и международных стандартов
- ASTM D6075 Standard Test Method for Cracking Resistance of Leather
- 59
- ASTM D6075 Standard Test Method for Cracking Resistance of Leather
- 59.140
- ASTM D6075 Standard Test Method for Cracking Resistance of Leather
- 59.140.30
- ASTM D1814 Standard Test Method for Measuring Thickness of Leather Units
- ASTM D1813 Standard Test Method for Measuring Thickness of Leather Test Specimens
- ASTM D2210 Standard Test Method for Grain Crack and Extension of Leather by the Mullen Test
- ASTM D2322 Standard Test Method for Resistance of Shoe Upper Leather to Artificial Perspiration
- ASTM D1610 Standard Practice for Conditioning Leather and Leather Products for Testing
- Картотека зарубежных и международных стандартов
ASTM International
Standard Test Method for Abrasion Resistance of Leather (Rotary Platform, Abraser Method)
N D7255
Annotation
This test method covers the determination of the abrasion resistance of leather using the rotary platform abraser.
NOTE 1—This test method is similar but not equivalent to ISO 17076-1, and results should not be directly compared between the two methods.
The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard.
This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and to determine the applicability of regulatory limitations prior to use.
Автоматический перевод:
Стандартный метод испытаний для износостойкости кожи (ротационная платформа, метод абразивного материала)
Этот метод испытаний покрывает определение износостойкости кожи с помощью ротационного абразивного материала платформы.
ПРИМЕЧАНИЕ 1 — Этот метод испытаний подобен, но не эквивалентен ISO 17076-1, и результаты не должны быть непосредственно сравнены между этими двумя методами.