ASTM B839 Standard Test Method for Residual Embrittlement in Metallic Coated, Externally Threaded Articles, Fasteners, and Rod-Inclined Wedge Method
Данный раздел/документ содержится в продуктах:
- Техэксперт: Машиностроительный комплекс
- Картотека зарубежных и международных стандартов
- BSI BS ISO 16111 Transportable gas storage devices - Hydrogen absorbed in reversible metal hydride
- 71
- ASTM F2832 Standard Guide for Accelerated Corrosion Testing for Mechanical Fasteners
- ASME B18.12 Glossary of Terms for Mechanical Fasteners
- ASME B18.10 Track Bolts and Nuts
- ASTM A183 Standard Specification for Carbon Steel Track Bolts and Nuts
- ASTM F606/F606M REV A Standard Test Methods for Determining the Mechanical Properties of Externally and Internally Threaded Fasteners, Washers, Direct Tension Indicators, and Rivets
- ASTM A183 Standard Specification for Carbon Steel Track Bolts and Nuts
- ASME B18.10 Track Bolts and Nuts
- ASME B18.12 Glossary of Terms for Mechanical Fasteners
- ASME B18.12 Glossary of Terms for Mechanical Fasteners
- ASME B18.10 Track Bolts and Nuts
- ASTM A183 Standard Specification for Carbon Steel Track Bolts and Nuts
- ASTM F606/F606M REV A Standard Test Methods for Determining the Mechanical Properties of Externally and Internally Threaded Fasteners, Washers, Direct Tension Indicators, and Rivets
- ASTM A183 Standard Specification for Carbon Steel Track Bolts and Nuts
- ASME B18.10 Track Bolts and Nuts
- ASME B18.10 Track Bolts and Nuts
- ASTM A183 Standard Specification for Carbon Steel Track Bolts and Nuts
- ASTM F606/F606M REV A Standard Test Methods for Determining the Mechanical Properties of Externally and Internally Threaded Fasteners, Washers, Direct Tension Indicators, and Rivets
- ASTM A183 Standard Specification for Carbon Steel Track Bolts and Nuts
- ASTM A183 Standard Specification for Carbon Steel Track Bolts and Nuts
- ASTM F606/F606M REV A Standard Test Methods for Determining the Mechanical Properties of Externally and Internally Threaded Fasteners, Washers, Direct Tension Indicators, and Rivets
- ASTM F606/F606M REV A Standard Test Methods for Determining the Mechanical Properties of Externally and Internally Threaded Fasteners, Washers, Direct Tension Indicators, and Rivets
- ASTM F2437 Standard Specification for Carbon and Alloy Steel Compressible-Washer-Type Direct Tension Indicators for Use with Cap Screws, Bolts, Anchors, and Studs
- ASTM A449 Standard Specification for Hex Cap Screws, Bolts and Studs, Steel, Heat Treated, 120/ 105/90 ksi Minimum Tensile Strength, General Use
- ASTM F436 Standard Specification for Hardened Steel Washers
- Картотека зарубежных и международных стандартов
ASTM International
Standard Test Method for Residual Embrittlement in Metallic Coated, Externally Threaded Articles, Fasteners, and Rod-Inclined Wedge Method
N B839
Annotation
This test method covers the determination of, on a statistical basis, the probability of the existence of hydrogen embrittlement or degradation in:
A batch of barrel electroplated, autocatalytic plated, phosphated, or chemically processed threaded articles or fasteners and
A batch of rack plated threaded articles, fasteners, or rod.
Industrial practice for threaded articles, fasteners, and rod has evolved three graduated levels of test exposure to ensure reduced risk of hydrogen embrittlement (see Section 3). These levels have evolved from commercial applications having varying levels of criticality. In essence, they represent the confidence level that is required. They also represent the time that finished goods are held before they can be shipped and used. This time equates to additional cost to the manufacturer that may of necessity be added to the cost of the finished goods.
This test method is applicable to threaded articles, fasteners, and rod made from steel with 1000 MPa (with corresponding hardness values of 300 HV10 kgf, 303 HB, or 31 HRc) or surface hardened threaded articles, fasteners, or rod.
This test method shall be carried out after hydrogen embrittlement relief heat treatment in accordance with the requirements of Guide B850. It may also be used for assessing differences in processing solutions, conditions, and techniques. This test method has two main functions: first, when used with a statistical sampling plan it can be used for lot acceptance or rejection, and second, it can be used as a control test to determine the effectiveness of the various processing steps including pre- and post-baking treatments to reduce the mobile hydrogen in the articles, fasteners, or rod. While this test method is capable of indicating those items that are embrittled to the extent defined in Section 3, it does not guarantee complete freedom from embrittlement.