ASTM F2660 Standard Test Method for Qualifying Coatings for Use on A490 Structural Bolts Relative to Environmental Hydrogen Embrittlement
Данный раздел/документ содержится в продуктах:
- Техэксперт: Машиностроительный комплекс
- Картотека зарубежных и международных стандартов
- ASTM F3043 Standard Specification for “Twist Off” Type Tension Control Structural Bolt/Nut/Washer Assemblies, Alloy Steel, Heat Treated, 200 ksi Minimum Tensile Strength
- 21
- ASTM F3141 Standard Guide for Total Knee Replacement Loading Profiles
- ASTM E2624 Standard Practice for Torque Calibration of Testing Machines and Devices
- ASTM E2624 Standard Practice for Torque Calibration of Testing Machines and Devices
- ASTM E2428 REV A Standard Practice for Calibration and Verification of Torque Transducers
- ASTM E2624 Standard Practice for Torque Calibration of Testing Machines and Devices
- ASTM E2207 Standard Practice for Strain-Controlled Axial-Torsional Fatigue Testing with Thin - Walled Tubular Specimens
- ASTM E1417/E1417M Standard Practice for Liquid Penetrant Testing
- ASTM F519 Standard Test Method for Mechanical Hydrogen Embrittlement Evaluation of Plating/ Coating Processes and Service Environments
- Картотека зарубежных и международных стандартов
ASTM International
Standard Test Method for Qualifying Coatings for Use on A490 Structural Bolts Relative to Environmental Hydrogen Embrittlement
N F2660
Annotation
This test method defines the procedures and tests to evaluate the effect of a coating system on the susceptibility to environmental hydrogen embrittlement (EHE) of an ASTM A490 high strength structural bolt.
This test method shall qualify a coating system for use with any size of A490 bolts (that is, to 1- in.) high strength structural bolts, relative to EHE.
The characteristic to be evaluated by this test method is the susceptibility to EHE caused by hydrogen generated from corrosion protection of the steel bolt by sacrificial galvanic corrosion of the coating. Testing shall be performed on coated, specimen ASTM A490 bolts manufactured to the maximum susceptible tensile strength values (see Table 1) of the bolt (see Section 5 Specimen Bolt Requirements). The internal hydrogen embrittlement (IHE) susceptibility will also be inherently evaluated when the EHE is tested through this test method. There is no need for a separate IHE susceptibility test.
The values stated in inch-pound units are to be regarded as standard. No other units of measurement are included in this standard.
This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.