SAE AMS4221E Aluminum Alloy, Plate 4.4Cu - 1.5Mg - 0.60Mn (2124-T8151) Solution Heat Treated, Stress Relieved, and Precipitation Heat Treated - UNS A92124
Данный раздел/документ содержится в продуктах:
- Техэксперт: Машиностроительный комплекс
- Картотека зарубежных и международных стандартов
- ASTM D6841 Standard Practice for Calculating Design Value Treatment Adjustment Factors for Fire-Retardant-Treated Lumber
- 13
- ASTM D6841 Standard Practice for Calculating Design Value Treatment Adjustment Factors for Fire-Retardant-Treated Lumber
- 13.220
- ASTM D6841 Standard Practice for Calculating Design Value Treatment Adjustment Factors for Fire-Retardant-Treated Lumber
- 13.220.50
- 79
- ASTM D9 Standard Terminology Relating to Wood and Wood-Based Products
- ASTM F547 Standard Terminology of Nails for Use with Wood and Wood-Base Materials
- ASTM F680 Standard Test Methods for Nails
- ASTM F1667 Standard Specification for Driven Fasteners: Nails, Spikes, and Staples
- ASTM B660 Standard Practices for Packaging/Packing of Aluminum and Magnesium Products
- Картотека зарубежных и международных стандартов
SAE International
Aluminum Alloy, Plate 4.4Cu - 1.5Mg - 0.60Mn (2124-T8151) Solution Heat Treated, Stress Relieved, and Precipitation Heat Treated - UNS A92124
N AMS4221E
Annotation
Form
This specification covers an aluminum alloy in the form of plate 1.500 inches (38.10 mm) to 6.000 inches (152.40 mm) in nominal thickness (see 8.4).
Applications
This plate has been used typically for parts requiring a high level of mechanical properties up to 300 °F (149 °C), but usage is not limited to such applications.
Certain design and fabrication procedures may cause plate to become susceptible to stress-corrosion cracking; ARP823 recommends practices to minimize such conditions.
Автоматический перевод:
Алюминиевый сплав, пластина 4.4Cu - Mn на 1.5 мг - 0.60 (2124-T8151) обработанное термически решение, облегченное напряжение, и обработанные термически осадки - UNS A92124
Форма
Эта спецификация касается алюминиевого сплава в форме пластины 1.500 дюйма (38.10 мм) к 6.000 дюймов (152.40 мм) в номинальной толщине (см. 8.4).
Применения
Эта пластина обычно использовалась для частей, требующих высокого уровня механических свойств до 300 °F (149 °C), но использование не ограничено такими применениями.