International Electrotechnical Commission

Nanomanufacturing – Key control characteristics – Part 6-4: Graphene – Surface conductance measurement using resonant cavity - Edition 1.0
 N TS 62607-6-4

Annotation

This part of IEC 62607 establishes a method for determining the surface conductance of twodimensional (2D) single-layer or multi-layer atomically thin nano-carbon graphene structures. These are synthesized by chemical vapour deposition (CVD), epitaxial growth on silicon carbide (SiC), obtained from reduced graphene oxide (rGO) or mechanically exfoliated from graphite [3]. The measurements are made in an air filled standard R100 rectangular waveguide configuration, at one of the resonant frequency modes, typically at 7 GHz [4].

Surface conductance measurement by resonant cavity involves monitoring the resonant frequency shift and change in the quality factor before and after insertion of the specimen into the cavity in a quantitative correlation with the specimen surface area. This measurement does not explicitly depend on the thickness of the nano-carbon layer. The thickness of the specimen does not need to be known, but it is assumed that the lateral dimension is uniform over the specimen area.

Автоматический перевод:

Нанопроизводство – Ключ управляет характеристиками – Часть 6-4: Графен – Поверхностное измерение проводимости с помощью резонатора - Издание 1.0

Эта часть IEC 62607 устанавливает метод для определения поверхностной проводимости двумерных (2D) одноуровневых или многоуровневых атомарно тонких наноуглеродных графеновых структур. Они синтезируются химическим паровым осаждением (CVD), эпитаксиальным ростом на кремниевом карбиде (SiC), получили из уменьшенной графеновой окиси (rGO) или механически расслоились от графита [3]. Измерения сделаны в воздухе, заполненном стандартный R100 прямоугольная конфигурация волновода, в одном из резонирующих режимов частоты, обычно в 7 GHz [4].