ASTM A900/A900M Standard Test Method for Lamination Factor of Amorphous Magnetic Strip
Данный раздел/документ содержится в продуктах:
- Техэксперт: Машиностроительный комплекс
- Картотека зарубежных и международных стандартов
- ASTM A1054 Standard Specification for Sintered Ceramic Ferrite Permanent Magnets
- 29
- ASTM A1054 Standard Specification for Sintered Ceramic Ferrite Permanent Magnets
- 29.030
- ASTM A1009 Standard Specification for Soft Magnetic MnZn Ferrite Core Materials for High Frequency (10 kHz-1 MHz) Power Transformer and Filter Inductor Applications
- ASTM A1013 Standard Test Method for High-Frequency (10 KHz-1 MHz) Core Loss of Soft Magnetic Core Components at Controlled Temperatures Using the Voltmeter-Ammeter-Wattmeter Method
- 29.100
- ASTM A1009 Standard Specification for Soft Magnetic MnZn Ferrite Core Materials for High Frequency (10 kHz-1 MHz) Power Transformer and Filter Inductor Applications
- ASTM A1013 Standard Test Method for High-Frequency (10 KHz-1 MHz) Core Loss of Soft Magnetic Core Components at Controlled Temperatures Using the Voltmeter-Ammeter-Wattmeter Method
- ASTM A1009 Standard Specification for Soft Magnetic MnZn Ferrite Core Materials for High Frequency (10 kHz-1 MHz) Power Transformer and Filter Inductor Applications
- ASTM A1009 Standard Specification for Soft Magnetic MnZn Ferrite Core Materials for High Frequency (10 kHz-1 MHz) Power Transformer and Filter Inductor Applications
- ASTM A1013 Standard Test Method for High-Frequency (10 KHz-1 MHz) Core Loss of Soft Magnetic Core Components at Controlled Temperatures Using the Voltmeter-Ammeter-Wattmeter Method
- ASTM A1013 Standard Test Method for High-Frequency (10 KHz-1 MHz) Core Loss of Soft Magnetic Core Components at Controlled Temperatures Using the Voltmeter-Ammeter-Wattmeter Method
- ASTM A34/A34M Standard Practice for Sampling and Procurement Testing of Magnetic Materials
- ASTM A977/A977M Standard Test Method for Magnetic Properties of High-Coercivity Permanent Magnet Materials Using Hysteresigraphs
- ASTM A340 Standard Terminology of Symbols and Definitions Relating to Magnetic Testing
- ASTM A901 Standard Specification for Amorphous Magnetic Core Alloys, Semi-Processed Types
- Картотека зарубежных и международных стандартов
ASTM International
Standard Test Method for Lamination Factor of Amorphous Magnetic Strip
N A900/A900M
Annotation
This test method covers measurements of lamination factor (Note 1) of a specimen composed of strips cut from amorphous magnetic material. It is suitable for the determination of lamination factor for thin, flat case, metallic strip ranging in width from 0.25 to 8.00 in. [6.35 mm to 203 mm] and in thickness from 0.0005 to 0.005 in. [12.7 to 127 m].
NOTE 1—Lamination factor is also termed space factor or stacking factor.
The values and equations stated in customary (egs-emu and inch-pound) or SI units are to be regarded separately as standard. Within this standard, SI units are shown in brackets. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in nonconformance with this standard.
This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.
Автоматический перевод:
Метод стандартной пробы для фактора расслоения аморфной магнитной полосы
Этот метод тестирования покрывает измерения фактора расслоения (Примечание 1) экземпляра, составленного из полос, сокращенных из аморфного магнитного материала. Это подходит для определения фактора расслоения для тонкого, плоского случая, металлическая полоса, располагающаяся по ширине от 0.25 до 8.00 дюймов. [6.35 мм к 203 мм] и в толщине от 0.0005 до 0.005 дюймов. [12.7 к 127 m].