ASTM B595 Standard Specification for Sintered Aluminum Structural Parts
Данный раздел/документ содержится в продуктах:
- Техэксперт: Машиностроительный комплекс
- Картотека зарубежных и международных стандартов
- ASTM B983 REV A Standard Specification for Precipitation Hardened or Cold Worked, Seamless Nickel Alloy Pipe and Tube
- 23
- ASME B31.5 Refrigeration Piping and Heat Transfer Components
- ASTM B43 Standard Specification for Seamless Red Brass Pipe, Standard Sizes
- ASTM B43 Standard Specification for Seamless Red Brass Pipe, Standard Sizes
- ASTM B687 Standard Specification for Brass, Copper, and Chromium-Plated Pipe Nipples
- ASTM B706 Standard Specification for Seamless Copper Alloy (UNS No. C69100) Pipe and Tube
- ASTM B193 Standard Test Method for Resistivity of Electrical Conductor Materials
- ASTM B624 Standard Specification for High-Strength, High-Conductivity Copper-Alloy Wire for Electronic Application
- ASTM E8/E8M REV A Standard Test Methods for Tension Testing of Metallic Materials
- Картотека зарубежных и международных стандартов
ASTM International
Standard Specification for Sintered Aluminum Structural Parts
N B595
Annotation
This specification covers sintered aluminum structural parts made primarily from aluminum powders to which controlled amounts of master alloys or elemental copper, magnesium, and silicon have been added by mixing.
This specification covers the following variables:
Composition—Depending upon levels of copper, magnesium, and silicon content, two grades, and
Density—Type.
Parts ordered to this specification will be in one of the following conditions:
As-sintered,
As-repressed for additional density, or
All other conditions plus heat treated.
With the exception of the values for density, for which the use of the gram per cubic centimeter unit is long-standing industry practice, the values stated in SI units are to be regarded as the standard.
Автоматический перевод:
Стандартная спецификация для пористых алюминиевых структурных частей
Эти покрытия спецификации спекли алюминиевые структурные части, сделанные, прежде всего, от алюминиевых порошков, до которых суммы, которыми управляют, основных сплавов или элементной меди, магния и кремния были добавлены путем смешивания.