ASTM A659/A659M Standard Specification for Commercial Steel (CS), Sheet and Strip, Carbon (0.16 Maximum to 0.25 Maximum Percent), Hot-Rolled
Данный раздел/документ содержится в продуктах:
- Техэксперт: Машиностроительный комплекс
- Картотека зарубежных и международных стандартов
- ASTM C844 Standard Specification for Application of Gypsum Base to Receive Gypsum Veneer Plaster
- ASTM C1002 Standard Specification for Steel Self-Piercing Tapping Screws for Application of Gypsum Panel Products or Metal Plaster Bases to Wood Studs or Steel Studs
- 21
- ASTM C1002 Standard Specification for Steel Self-Piercing Tapping Screws for Application of Gypsum Panel Products or Metal Plaster Bases to Wood Studs or Steel Studs
- 21.060
- ASTM C1002 Standard Specification for Steel Self-Piercing Tapping Screws for Application of Gypsum Panel Products or Metal Plaster Bases to Wood Studs or Steel Studs
- 21.060.10
- ASTM C1780 Standard Practice for Installation Methods for Adhered Manufactured Stone Masonry Veneer
- 91
- ASTM C1780 Standard Practice for Installation Methods for Adhered Manufactured Stone Masonry Veneer
- ASTM C847 REV A Standard Specification for Metal Lath
- ASTM A568/A568M Standard Specification for Steel, Sheet, Carbon, Structural, and High-Strength, Low-Alloy, Hot-Rolled and Cold-Rolled, General Requirements for
- Картотека зарубежных и международных стандартов
ASTM International
Standard Specification for Commercial Steel (CS), Sheet and Strip, Carbon (0.16 Maximum to 0.25 Maximum Percent), Hot-Rolled
N A659/A659M
Annotation
This specification covers hot-rolled carbon steel (CS) sheet and strip, in coils and cut lengths, in which the maximum of the specified carbon range is over 0.15 and not over 0.25 % and the maximum of the specified manganese range is not over 0.90 %. This material is ordered to chemical composition.
This specification is not applicable to the steels covered by Specification A 635/A 635M.
The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard.
*A Summary of Changes section appears at the end of this standard.
Автоматический перевод:
Стандартная спецификация для стали промышленного производства (CS), листа и полосы, углерода (0.16 максимума к 0.25 максимальным процентам), горячекатаный
Эта спецификация покрывает горячекатаный лист углеродистой стали (CS) и полосу, в обмотках и продолжительности сокращения, в которые максимум указанного углеродного диапазона, более чем 0.15 и не более чем 0.25% и максимум указанного марганцевого диапазона не составляют более чем 0.90%. Этот материал упорядочивается химическому составу.