International Organization for Standardization

Destructive tests on welds in metallic materials - Hardness testing - Part 2: Microhardness testing of welded joints - Second Edition
 N 9015-2

Annotation

This part of ISO 9015 specifies microhardness testing on transverse sections of welded joints of metallic materials with high hardness gradients. It covers Vickers hardness tests in accordance with ISO 6507-1, normally with test loads of 0,98 N to less than 49 N (HV 0,1 to less than HV 5).

NOTE Testing ensures that the highest and/or the lowest level of hardness of both parent materials (in the case of dissimilar materials both parent materials) and weld metal is determined.

This part of ISO 9015 is not applicable to hardness testing of welds with loads of 49,03 N and above, which is covered by ISO 9015-1.

This part of ISO 9015 is not applicable to Vickers hardness testing of resistance spot, projection and seam welds, which is covered by ISO 14271.

This part of ISO 9015 is not applicable to hardness testing of very narrow welds, e.g. those typically produced by laser and electron beam welding (see ISO 22826).

Автоматический перевод:

Разрушительные тесты на сварках в металлических материалах - тестировании Твердости - Часть 2: тестирование микротвердости сварных стыков - Второй Выпуск

Эта часть ISO 9015 указывает тестирование микротвердости на поперечных сечениях сварных стыков металлических материалов с высокими градиентами твердости. Это покрывает тесты твердости Викерса в соответствии с ISO 6507-1, обычно с контрольными нагрузками 0,98 Н меньше чем к 49 Н (HV 0,1 к меньше, чем HV 5).