ASTM International

Standard Test Method for Determination of Slow Crack Growth Parameters of Advanced Ceramics by Constant Stress-Rate Flexural Testing at Elevated Temperatures
 N C1465

Annotation

This test method covers the determination of slow crack growth (SCG) parameters of advanced ceramics by using constant stress-rate flexural testing in which flexural strength is determined as a function of applied stress rate in a given environment at elevated temperatures. The strength degradation exhibited with decreasing applied stress rate in a specified environment is the basis of this test method which enables the evaluation of slow crack growth parameters of a material.

NOTE 1—This test method is frequently referred to as "dynamic fatigue" testing (Refs (1-3))2 in which the term "fatigue" is used interchangeably with the term "slow crack growth." To avoid possible confusion with the "fatigue" phenomenon of a material which occurs exclusively under cyclic loading, as defined in Terminology E1823, this test method uses the term "constant stress-rate testing" rather than "dynamic fatigue" testing.

NOTE 2—In glass and ceramics technology, static tests of considerable duration are called "static fatigue" tests, a type of test designated as stress-rupture (Terminology E1823).

This test method is intended primarily to be used for negligible creep of test specimens, with specific limits on creep imposed in this test method.

This test method applies primarily to advanced ceramics that are macroscopically homogeneous and isotropic. This test method may also be applied to certain whisker- or particlereinforced ceramics that exhibit macroscopically homogeneous behavior.

This test method is intended for use with various test environments such as air, vacuum, inert, and any other gaseous environments.