ASTM C1212 Standard Practice for Fabricating Ceramic Reference Specimens Containing Seeded Voids
Данный раздел/документ содержится в продуктах:
- Техэксперт: Машиностроительный комплекс
- Картотека зарубежных и международных стандартов
- ASTM F3192 Standard Specification for High-Purity Copper Sputtering Target Used for Through- Silicon Vias (TSV) Mettalization
- ASTM F3166 Standard Specification for High-Purity Titanium Sputtering Target Used for Through- Silicon Vias (TSV) Metallization
- ASTM F1512 Standard Practice for Ultrasonic C-Scan Bond Evaluation of Sputtering Target-Backing Plate Assemblies
- ASTM E1736 Standard Practice for Acousto-Ultrasonic Assessment of Filament-Wound Pressure Vessels
- ASTM E1001 Standard Practice for Detection and Evaluation of Discontinuities by the Immersed Pulse-Echo Ultrasonic Method Using Longitudinal Waves
- ASTM B331 Standard Test Method for Compressibility of Metal Powders in Uniaxial Compaction
- ASTM C1336 Standard Practice for Fabricating Non-Oxide Ceramic Reference Specimens Containing Seeded Inclusions
- ASTM C373 REV A Standard Test Method for Water Absorption, Bulk Density, Apparent Porosity, and Apparent Specific Gravity of Fired Whiteware Products, Ceramic Tiles, and Glass Tiles
- Картотека зарубежных и международных стандартов
ASTM International
Standard Practice for Fabricating Ceramic Reference Specimens Containing Seeded Voids
N C1212
Annotation
This practice describes procedures for fabricating both green and sintered test bars of silicon carbide and silicon nitride containing both internal and surface voids at prescribed locations.
The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard.
This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.
Автоматический перевод:
Утвержденный технологический процесс для производства керамических справочных экземпляров, содержащих отобранные пустоты
Эта практика описывает процедуры для производства и зеленые и пористые испытательные бруски карбида кремния и нитрида кремния, содержащего и внутренние и поверхностные пустоты в заданных местах.
Значения, указанные в единицах СИ, должны рассматриваться как стандарт. Никакие другие единицы измерения не включены в этот стандарт.