Aerospace series - Zinc-Nickel (12 %-16 % Ni) plating of steels with specified tensile strength ? 1 450 MPa, copper alloys, nickel alloys and aluminium alloys for parts and fasteners
 N EN 4826

Annotation

This European Standard specifies the plating of a Zinc-Nickel (12 % to 16 %) alloy on mechanical parts and fasteners in steels (Rm 1 450 MPa), stainless steels (Rm 1 450 MPa), copper alloys, nickel alloys and aluminium alloys (not applicable for electrical components), as well as the passivation and lubricant finishing that can be associated to them. The Zinc-Nickel process is an electrolytic plating process under controlled current allowing to deposit a Zinc-Nickel layer from, most often, an alkaline electrolyte. Alkaline Zinc-Nickel is only considered in this standard.

The purpose of this standard is to give technical and quality requirements of Zinc-Nickel plating. It doesn't give complete in-house process instructions, these shall be given in the manufacturers detailed process instructions.

Автоматический перевод:

Космический ряд - Цинковый Никель (12%-16% Ni) металлизация сталей с указанной прочностью на растяжение 1 450 МПа, медными сплавами, сплавами никеля и алюминием сплавляет для частей и застежек

Этот европейский стандарт определяет металлизацию Цинкового Никеля (12% к 16%) сплав на механических деталях и застежках в сталях (Комната 1 450 МПа), нержавеющая сталь (Комната 1 450 МПа), медные сплавы, сплавы никеля и алюминиевые сплавы (не применимый для электрических составляющих), а также пассивирование и смазка, заканчивающаяся, который может быть связан с ними. Процесс Цинкового Никеля является процессом нанесения электролитического покрытия под управляемым током, позволяющим внести уровень Zinc-Nickel от, чаще всего, щелочной электролит. Щелочной Цинковый Никель только рассматривают в этом стандарте.