Comitato Elettrotecnico Italiano

Materials for printed boards and other interconnecting structures Part 2-30: Reinforced base materials clad and unclad - Non-halogenated epoxide modified cyanate ester woven glass laminate sheets of defined flammability (vertical burning test), copper-clad
 N EN 61249-2-30

Annotation

This part of IEC 61249 gives requirements for properties of non-halogenated epoxide modified cyanate ester woven glass laminate of defined flammability (vertical burning test), copper-clad in thicknesses of 0,03 mm up to 1,60 mm. The flammability rating is achieved through the use of non-halogenated inorganic and/or organic compounds acting as fire retardants. These fire retardants are contained as part of polymeric structure or in addition to it. The glass transition temperature is defined to be 160 °C minimum.

Some property requirements may have several classes of performance. The class desired should be specified on the purchase order, otherwise the default class of material may be supplied.

Автоматический перевод:

Материалы для печатных плат и другой взаимосвязанной Части 2-30 структур: Усиленные основные материалы, одетые и голые - Негалогенизировавший эпоксид, изменили сложный эфир цианата сотканные стеклянные листы ламината определенной воспламеняемости (вертикальный горящий тест), медно-одетый

Эта часть IEC 61249 дает требования для свойств измененного сложного эфира цианата негалогенизировавшего эпоксида сотканный стеклянный ламинат определенной воспламеняемости (вертикальный горящий тест), медно-одетый в толщины 0,03 мм до 1,60 мм. Оценка воспламеняемости достигается с помощью негалогенизировавших неорганических и/или органических соединений, действующих как замедлители огня. Эти замедлители огня содержатся как часть полимерной структуры или в дополнение к нему. Температура стеклования определяется, чтобы быть 160 °C минимумами.