ASME STP-PT-058 TEMPER BEAD QUALIFICATION HARDNESS ACCEPTANCE CRITERIA
Данный раздел/документ содержится в продуктах:
- Техэксперт: Машиностроительный комплекс
- Картотека зарубежных и международных стандартов
- API 570 Piping Inspection Code: In-service Inspection, Rating, Repair, and Alteration of Piping Systems - Third Edition
- ASME B31.3 Process Piping - Includes Interpretation 23
- API 510 Pressure Vessel Inspection Code: In-Service Inspection, Rating, Repair, and Alteration - Ninth Edition: Includes Errata April 2009
- BSI BS EN 1143-1 Secure storage units - Requirements, classification and methods of test for resistance to burglary Part 1: Safes, ATM safes, strongroom doors and strongrooms
- 13
- BSI BS EN 1143-1 Secure storage units - Requirements, classification and methods of test for resistance to burglary Part 1: Safes, ATM safes, strongroom doors and strongrooms
- 13.310
- BSI BS 7958 Closed circuit television (CCTV) - Management and operation - Code of practice
- BSI BS 8220-3 Guide for security of buildings against crime - Part 3: Storage, industrial and distribution premises
- BSI BS EN 1011-1 Welding - Recommendations for welding of metallic materials Part 1: General guidance for arc welding
- Картотека зарубежных и международных стандартов
ASME International
TEMPER BEAD QUALIFICATION HARDNESS ACCEPTANCE CRITERIA
N STP-PT-058
Annotation
INTRODUCTION
Post-weld heat treatment (PWHT) is applied to steel assemblies in order to reduce the likelihood of brittle fracture; this is achieved through the combined effect of a reduction in residual stresses and the tempering of hard, brittle microstructures.
For fabrications where the need for a welded repair has been identified, but for which a post-weld heat treatment would be impractical or expensive, it is possible to affect a repair by using a procedure which is intended to give rise to significant refinement and tempering of the heat-affected zone (HAZ) microstructure. Furthermore, for materials operating within the creep regime, and particularly for a repair with near-matching weld metal, whilst the imposition of a PWHT would substantially reduce the level of residual stress, it is likely to shorten creep life by inducing precipitate growth and substructure recovery in the HAZ.
Several slightly different approaches have been developed for repair without PWHT, from conventional buttering to a half-bead technique, and later a two-layer approach. A schematic diagram of a weldment, together with the relevant regions of the Fe-C phase diagram is shown in Figure 1 [1]. The principle of the various controlled deposition repair strategies is that weld beads in the first layer are overlapped such that at least part of the coarse-grained region produced by the previous bead is replaced with fine-grained HAZ. A second layer, with appropriate penetration, can achieve further refinement, and further layers may be added to achieve tempering.