CEN CEN/TS 16011 Plastics - Recycled plastics - Sample preparation
Данный раздел/документ содержится в продуктах:
- Техэксперт: Машиностроительный комплекс
- Картотека зарубежных и международных стандартов
- AFNOR NF EN 12099 Plastics piping systems. Polyethylene piping materials and components. Determination of volatile content.
- 23
- AFNOR NF EN 12099 Plastics piping systems. Polyethylene piping materials and components. Determination of volatile content.
- 23.040
- DIN EN 12048 Solid fertilizers and liming material - Determination of moisture content - Gravimetric method by drying at (105 ± 2) °C (ISO 8190:1992, modified)
- DIN EN 16357 Carbonate liming materials - Determination of reactivity - Automatic titration method with citric acid
- DIN EN 16357 Carbonate liming materials - Determination of reactivity - Automatic titration method with citric acid
- DIN EN 12948 Liming materials - Determination of size distribution by dry and wet sieving
- DIN ISO 565 Test sieves - Metal wire cloth, perforated metal plate and electroformed sheet - Nominal sizes of openings (ISO 565:1990)
- DIN EN 15346 Plastics - Recycled plastics - Characterization of poly(vinyl chloride) (PVC) recyclates
- Картотека зарубежных и международных стандартов
European Committee for Standardization
Plastics - Recycled plastics - Sample preparation
N CEN/TS 16011
Annotation
This Technical Specification specifies the preparation of samples of recycled plastics prior to testing and takes account of the specifics of the material.
Sample preparation should avoid any process that causes 'de-mixing' of the sample. Following preparation, the sample should remain representative.
The behaviour of contaminants should be carefully analysed and observed to ensure this is homogeneous.
This Technical Specification does not address any legal or product safety issues.
Автоматический перевод:
Пластмассы - Рециклизованные пластмассы - Подготовка образцов
Эта Техническая спецификация указывает подготовку образцов рециклизованных пластмасс до тестирования и принимает во внимание специфические особенности материала.
Подготовка образцов должна избежать любого процесса, который вызывает 'расслоение' образца. Следующая подготовка, образец должен остаться представительным.